Evaluation of antioxidant cellulose nanocrystals and applications in gellan gum films

Criado, Paula; Fraschini, Carole; Salmieri, Stephane; Becher, Dorra; Safrany, Agnes; Lacroix, Monique (2015). Evaluation of antioxidant cellulose nanocrystals and applications in gellan gum films Industrial Biotechnology , vol. 11 , nº 1. p. 59-68. DOI: 10.1089/ind.2014.0017.

Ce document n'est pas hébergé sur EspaceINRS.

Résumé

The research described herein shows the treatment of cellulose nanocrystals (CNCs) led to antioxidant properties after 2 h of interaction with a redox pair—hydrogen peroxide (H2O2) and ascorbic acid (AA)—and 20 kGy irradiation. This procedure enhanced the surface of CNCs to react for 24 h with the antioxidant gallic acid (GA) at different mass ratios of CNC/GA (R=0.66 and 8). Each step of the modification was evaluated, but optimal results were found on CNC-H2O2-AA-γ-GA. Different analysis such as Fourier transform infrared spectroscopy exposed the apparition of a new band at 1730 cm−1, which can be explained by the formation of carbonyl groups on CNC. By studying the ultraviolet spectra of the different solutions, it was noticed that at wavelengths ∼290-nm intensity increases, showing a possible formation of aldehyde and carboxylic acids groups. This latter group was evaluated via conductometric titration, observing that CNC-H2O2-AA-γ-GA possesses 132 mmol COOH/kg and 8 mM Trolox eq/mL solution. A reduction in the thermal stability of CNC-H2O2-AA-γ-GA was found with thermogravimetric analysis, which confirms changes to the CNC surface. A 20% solution of the modified CNC-H2O2-AA-γ-GA was introduced onto a gellan gum matrix to create antioxidant film applications and enhanced mechanical properties. Improved (p≤0.05) tensile strength, tensile modulus, and water vapor permeability were observed with a decrease at the elongation at break in the film packaging formulation.

Type de document: Article
Mots-clés libres: -
Centre: Centre INRS-Institut Armand Frappier
Date de dépôt: 28 sept. 2017 18:47
Dernière modification: 28 sept. 2017 18:47
URI: http://espace.inrs.ca/id/eprint/3169

Actions (Identification requise)

Modifier la notice Modifier la notice